Zirconia wani abu ne da ke da ƙarfin injina da ƙarfin karyewa a zafin jiki.An ƙara zirconia (ZrO2) tare da 3mol% Y2O3 barga zirconia (PSZ).Domin barbashi diamita na PSZ abu ne karami, shi za a iya sarrafa tare da high madaidaici, da kuma aikace-aikace a daidai machining sassa kamar molds ne fadada.Bugu da ƙari, kuma za a iya amfani da kayan aikin masana'antu, sassa masu haɗin kai da murkushe matsakaicin kayan aiki.Za'a iya amfani da tauri mai ƙarfi na PSZ don yin maɓuɓɓugan ruwa na musamman, kuma ana amfani da shi sosai a cikin wuƙaƙen yumbu na gida, slicer da sauran sassa.
Zirconia (ZrO2) Na manyan amfani
Mold da mold kayan aikin (molds iri-iri, daidaitaccen matsayi na daidaitawa, kayan aikin rufewa);sassa (classifier, iska kwarara niƙa, dutsen dutse niƙa);Kayan aiki na masana'antu (masu yankan masana'antu, injin slitter, mirgine latsa lebur);Abubuwan haɗin haɗi na gani (zobe na hatimi, hannun riga, ƙirar V-groove);Maɓuɓɓugar ruwa na musamman (ganin nada, bazarar farantin karfe);Kayayyakin mabukaci (ƙananan na'urar sukudireba, wuƙa yumbu, slicer).
Kayayyakin Kayayyaki
| Abu | 95% Alumina | 99% Alumina | Zirconia | Silicon carbide | SilikiNtsiri | AluminumNtsiri | Injin yumbu |
| Launi | fari | rawaya mai haske | fari | baki | baki | launin toka | fari |
| Yawan yawa (g/cm3) | 3.7g/cm 3 | 3.9g/cm 3 | 6.02g/cm 3 | 3.2g/cm 3 | 3.25g/cm 3 | 3.2g/cm 3 | 2.48g/cm 3 |
| Shakar Ruwa | 0% | 0% | 0% | 0% | 0% | 0% | 0% |
| Hardness (HV) | 23.7 | 23.7 | 16.5 | 33 | 20 | - | - |
| Ƙarfin Ƙarfi (MPa) | 300MPa | 400MPa | 1100MPa | 450MPa | 800MPa | 310MPa | 91MPa |
| Ƙarfin Ƙarfi (MPa) | 2500MPa | 2800MPa | 3600MPa | 2000MPa | 2600MPa | - | 340MPa |
| Modulus Na Matasa Na Nauyi | 300GPa | 300GPa | 320GPa | 450GPa | 290GPa | 310-350GPa | 65GPa |
| Rabon Poisson | 0.23 | 0.23 | 0.25 | 0.14 | 0.24 | 0.24 | 0.29 |
| Thermal Conductivity | 20W/m°C | 32W/m°C | 3W/m°C | 50W/m°C | 25W/m°C | 150W/m°C | 1.46W/m°C |
| Ƙarfin Dielectric | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm |
| Juyin Juriya (25 ℃) | > 1014Ω · cm | > 1014Ω · cm | > 1014Ω · cm | > 105Ω · cm | > 1014Ω · cm | > 1014Ω · cm | > 1014Ω · cm |